Department of Mechanical Engineering2024-11-0920191757-898110.1088/1757-899X/529/1/0120102-s2.0-85067844790https://hdl.handle.net/20.500.14288/2160We present an experimental investigation on the effects of the interphase energy anisotropy on the formation of three-phase growth microstructures during directional solidification (DS) of the β(In)-In2Bi-γ(Sn) ternary-eutectic system. Standard DS and rotating directional solidification (RDS) experiments were performed using thin alloy samples with real-time observation. We identified two main types of eutectic grains (EGs): (i) quasi-isotropic EGs within which the solidification dynamics do not exhibit any substantial anisotropy effect, and (ii) anisotropic EGs, within which RDS microstructures exhibit an alternation of locked and unlocked microstructures. EBSD analyses revealed (i) a strong tendency to an alignment of the In2Bi and γ(Sn) crystals (both hexagonal) with respect to the thin-sample walls, and (ii) the existence of special crystal orientation relationships (ORs) between the three solid phases in both quasi-isotropic and anisotropic EGs. We initiate a discussion on the dominating locking effect of the In2Bi-β(In) interphase boundary during quasi steady-state solidification, and the existence of strong crystal selection mechanisms during early nucleation and growth stages.pdfEngineeringEutecticsSolidificationConference proceedinghttps://doi.org/10.1088/1757-899X/529/1/012010N/ANOIR01618