Department of Physics2024-11-1020120022-231310.1016/j.jlumin.2011.07.0042-s2.0-80051802586http://dx.doi.org/10.1016/j.jlumin.2011.07.004https://hdl.handle.net/20.500.14288/17662We have performed detailed experiments to investigate the spectroscopic properties of a new type of tellurite based host doped with thulium: Tm2O3:(0.70)TeO2-(0.15)K2O-(0.15)Nb2O5 having Tm2O3 concentrations of 0.125, 0.25, 0.5, and 1.0 mol%. By performing a Judd-Ofelt analysis of the absorption bands, we obtained average radiative lifetimes of 2.57 +/- 0.20 and 0.35 +/- 0.01 ms for the H-3(4) and F-3(4) levels, respectively. Furthermore, we also observed that an increase in the Tm2O3 concentration from 0.125 to 1.0 mol% results in a decrease of the measured fluorescence lifetime from 814 to 439 mu s and from 258 to 47 mu s for the H-3(4) and F-3(4) levels, respectively, due to efficient non-radiative decay. The highest quantum efficiency of 32% was obtained for the sample doped with 0.125 mol% Tm2O3 for the H-3(4) level. Results show that cross relaxation becomes important as the ion concentration is increased, leading to the quenching of the 1460-nm band and enhancement of the 1860-nm emission. The highest emission cross section of 6.85 x 10(-21) Cm-2 measured for the 1860-nm band reveals the potential of this host for the development of 2-mu m lasers in bulk glass as well as fiber media. (C) 2011 Published by Elsevier B.V.OpticsJournal Article302662600021Q23208